Before starting the experiments, the absorbance of our inkjet ink was determined in to determine the values that should be expected in further analysis (figure 3).
 
Before starting the experiments, the absorbance of our inkjet ink was determined in to determine the values that should be expected in further analysis (figure 3).
  
 +
{{UBonn_HBRS/image|url=//2016.igem.org/wiki/images/1/18/T--UBonn_HBRS--deinking_absorbance_ink.png|alt=absorbance ink|class=100 borderless}}
 +
 +
==Filtration based deinking==
 +
{{UBonn_HBRS/image|url=//2016.igem.org/wiki/images/1/18/T--UBonn_HBRS--deinking_construction_1.jpg|alt=absorbance ink|class=100 borderless}}
  
 
To keep the scale of the experiments manageable, 50 mL falcons were chosen as containers for the small scale deinking.  
 
To keep the scale of the experiments manageable, 50 mL falcons were chosen as containers for the small scale deinking.  
Line 51: Line 55:
 
==Flow through analysis==
 
==Flow through analysis==
 
After the flow-through is produced, it is once again vortexed and 100 μm of the samples together with water as a blank are transferred into 96 well plates in order to measure the absorbance of it with the plate reader (in our laboratory, the Tecan Infinite 200 PRO multimode reader was used). The plate reader works as spectrophotometer, it compares the light intensity of the emitted light to the light intensity of the light detected after a passage through the sample.
 
After the flow-through is produced, it is once again vortexed and 100 μm of the samples together with water as a blank are transferred into 96 well plates in order to measure the absorbance of it with the plate reader (in our laboratory, the Tecan Infinite 200 PRO multimode reader was used). The plate reader works as spectrophotometer, it compares the light intensity of the emitted light to the light intensity of the light detected after a passage through the sample.
 +
 +
{{UBonn_HBRS/image|url=//2016.igem.org/wiki/images/1/18/T--UBonn_HBRS--deinking_absorbance_980.png|alt=absorbance ink 980|class=100 borderless}}
 +
 +
 
After the measurements the absolute absorbance is calculated (absorbance of sample at specific wavelength – blank at specific wavelength). According to the.....the most important wavelengths to evaluate deinking efficiency are 970 and 980 nm, for this reason we concentrated on them. However, the values at these two wavelengths are almost equal, for this reason, only one of them is presented in figure 5.  
 
After the measurements the absolute absorbance is calculated (absorbance of sample at specific wavelength – blank at specific wavelength). According to the.....the most important wavelengths to evaluate deinking efficiency are 970 and 980 nm, for this reason we concentrated on them. However, the values at these two wavelengths are almost equal, for this reason, only one of them is presented in figure 5.  
  
Line 61: Line 69:
 
8-bit grayscale values can vary between 0 (black paper) and 255 (white paper), all values in between describe different shades of gray thus the brightness of the paper. However, brightness alone does not describe paper quality, but it is one of the most important indicators, especially when the experiments are carried out with office waste paper.  
 
8-bit grayscale values can vary between 0 (black paper) and 255 (white paper), all values in between describe different shades of gray thus the brightness of the paper. However, brightness alone does not describe paper quality, but it is one of the most important indicators, especially when the experiments are carried out with office waste paper.  
 
Both sides of the resulting dry paper disks were scanned in 5 different places on an office scanner. Afterwards, the images were analysed and the grayscale value obtained with the program ImageJ. (figure 6)
 
Both sides of the resulting dry paper disks were scanned in 5 different places on an office scanner. Afterwards, the images were analysed and the grayscale value obtained with the program ImageJ. (figure 6)
 +
 +
{{UBonn_HBRS/image|url=//2016.igem.org/wiki/images/1/18/T--UBonn_HBRS--deinking_grayscale_comparis.png|alt=grayscale|class=100 borderless}}
 +
 +
  
 
==Flotation-based deinking==
 
==Flotation-based deinking==
 
In order to improve the deinking mechanism in our laboratory, the experiments were up-scaled. The apparatus and process itself now were much more similar to the ones used in industry (figure 7).
 
In order to improve the deinking mechanism in our laboratory, the experiments were up-scaled. The apparatus and process itself now were much more similar to the ones used in industry (figure 7).
 +
 +
{{UBonn_HBRS/image|url=//2016.igem.org/wiki/images/1/18/T--UBonn_HBRS--deinking_water_vs_std.png|alt=water vs standard|class=100 borderless}}
  
 
Chemical deinking was carried out using this experimental setup. Chemicals and 50 °C water were added to the beaker together with the pulp. The stirring was constant in order to mix the chemicals and fibers together. After the start of the air pump, foam, collecting ink, starts to form. For this reason, it is important to analyse foam properly.  
 
Chemical deinking was carried out using this experimental setup. Chemicals and 50 °C water were added to the beaker together with the pulp. The stirring was constant in order to mix the chemicals and fibers together. After the start of the air pump, foam, collecting ink, starts to form. For this reason, it is important to analyse foam properly.  
Line 70: Line 84:
 
==Ink removal==
 
==Ink removal==
 
Ca2+ ions are necessary in the deinking process. Previously no chemicals containing Ca2+ were added as they can originate straight from hard water or from paper itself. However, it was decided to add CaCl2 and test its effect on deinking. The experiment resulted in ink being separated completely from fibers as organic phase (figure 8).
 
Ca2+ ions are necessary in the deinking process. Previously no chemicals containing Ca2+ were added as they can originate straight from hard water or from paper itself. However, it was decided to add CaCl2 and test its effect on deinking. The experiment resulted in ink being separated completely from fibers as organic phase (figure 8).
 +
 +
 +
{{UBonn_HBRS/image|url=//2016.igem.org/wiki/images/1/18/T--UBonn_HBRS--deinking_black_things.jpg|alt=black things|class=100 borderless}}
 +
  
 
==Latest deinking system==
 
==Latest deinking system==
 
The newest deinking setup goes back to the small scale filtration-based deinking. The basic principle and used chemicals are the same as mentioned at the beginning. Only few things were changed: A kitchen mixer was used instead of vortexing machine, moreover, pulp after treatment was dried differently as it was decided to use the scanning method as the most reliable way to analyse paper deinking efficiency. For this reason bigger and flatter paper disks were needed.
 
The newest deinking setup goes back to the small scale filtration-based deinking. The basic principle and used chemicals are the same as mentioned at the beginning. Only few things were changed: A kitchen mixer was used instead of vortexing machine, moreover, pulp after treatment was dried differently as it was decided to use the scanning method as the most reliable way to analyse paper deinking efficiency. For this reason bigger and flatter paper disks were needed.
 
After filtrating the pulp-chemical mixture through the sieve, wet fibers were spread onto the lid of the well plate and were pressed lightly to flatten them. After one day, dry paper disks were scanned with the Li-Cor Odyssey infrared scanner and absorbance values at 700 nm were gained (figure 9). An office scanner was tested as well. However, it was not chosen because it may affect the value by adjusting the light when scanning.
 
After filtrating the pulp-chemical mixture through the sieve, wet fibers were spread onto the lid of the well plate and were pressed lightly to flatten them. After one day, dry paper disks were scanned with the Li-Cor Odyssey infrared scanner and absorbance values at 700 nm were gained (figure 9). An office scanner was tested as well. However, it was not chosen because it may affect the value by adjusting the light when scanning.
 +
 +
 +
{{UBonn_HBRS/image|url=//2016.igem.org/wiki/images/1/18/T--UBonn_HBRS--deinking_water_vs_std.png|alt=water vs standard|class=100 borderless}}
  
 
The data from figure 9 proves that the deinking and its analysis system in laboratory scale was established. For this reason, tests of citrate buffer and one of the enzyme, Xylanase, were started. However, all the experiments resulted in much darker paper even when compared to simply washed paper pulp (figure 10).
 
The data from figure 9 proves that the deinking and its analysis system in laboratory scale was established. For this reason, tests of citrate buffer and one of the enzyme, Xylanase, were started. However, all the experiments resulted in much darker paper even when compared to simply washed paper pulp (figure 10).
 +
 +
 +
{{UBonn_HBRS/image|url=//2016.igem.org/wiki/images/1/18/T--UBonn_HBRS--deinking_citrate😂.jpg|alt=water vs standard|class=100 borderless}}
  
 
Another problem is citrate buffer‘s crystallization. After the pulp is dried after treatment with citrate buffer, it tends to show higher values when scanning at 700 nm (meaning brighter paper). This is caused by the crystals of citrate buffer and leads to misinterpreting of results.
 
Another problem is citrate buffer‘s crystallization. After the pulp is dried after treatment with citrate buffer, it tends to show higher values when scanning at 700 nm (meaning brighter paper). This is caused by the crystals of citrate buffer and leads to misinterpreting of results.
 
Due to the lack of time further experiments could not be carried out. However, the laboratory scale deinking system is established and can give promising results when using enzymes to deink the paper.  
 
Due to the lack of time further experiments could not be carried out. However, the laboratory scale deinking system is established and can give promising results when using enzymes to deink the paper.  
 
{{UBonn_HBRS/footer}}
 
{{UBonn_HBRS/footer}}

Revision as of 21:32, 19 October 2016

Deinking

General Abstract

Deinking, the removal of ink particles from paper fibers, is a widely used procedure to recycle paper. Chemical deinking, the current standard, is known to perform this task efficiently. However, it requires large amounts of chemicals, which production has an extensive energy need and creates harmful byproducts. An alternative to chemical deinking is enzymatic deinking. As indicated by its name, chemicals are replaced by enzymes that are known to detach ink from fibers. The biological method is has a lower energy demand and the byproducts of an optimized bacterial culture can be negligible and would therefore cut the costs and the ecological footprint of the whole process. Moreover, it is shown that enzymatic deinking has a lower chemical oxygen demand (COD) content and thus results in a brighter and stronger paper product. The goal of this part of our project is to establish a reliable method to test enzymatic deinking efficiency and to deink paper by using a small scale apparatus, which would allow decentralized recycling of paper and, as a side effect, further lower the cost of deinking.


Pulp preparation

Inkjet type ink was chosen for tests in our experiments. It is an aqueous ink, mainly composed out of water, dyes, pigments and glycol. When printing, droplets of ink are added onto the paper. In our experiments, the ink was used to print on office printing paper. For this reason, the pulp is referred to as office waste paper (OW). Pulp preparation starts with printing a completely black sheet of paper and dividing it into equal parts. This sheet of paper is then mixed with white paper. In our experiments different ratios were used, based on the papers’ surface:

  • 100 % - fully black paper sheet,
  • 50 % - equal amounts of black and white paper
  • 25 % - a quarter black paper, the rest white
  • 0 % - completely white paper pulp.

After the paper sheets were divided and mixed, they were washed with 1L of 60°C warm water and mixed with a kitchen blender for around two minutes. Afterwards, the pulp was filtrated through a sieve and the washed out paper fibers were dried in a 70 °C heater for one day. In the next step, the pulp was scooped out and once more mixed with the kitchen mixer for two minutes. With the end of this step, the pulp was ready for the deinking experiments.


Industrial deinking procedure

The most commonly used industrial deinking method is called froth flotation. The principle behind this process is the separation of hydrophobic and hydrophilic particles in the pulp by a stream of air bubbles, after mechanical and chemical treatment of the paper pulp. In order to implement proper flotation-based deinking, a flotation cell is needed (figure 1).

Chemicals that are used for the chemical treatment are:

  • NaOH (sodium hydroxide) – alkaline solution needed for saponification, for pH adjustment and for increasing ink detachment effect.
  • C18H34O2 (oleic acid) – acts as surfactant (figure 2).
  • H2O2 (hydrogen peroxide) – bleaches the pulp and stops the darkening of fibers caused by sodium hydroxide.
  • Na2SiO3 (sodium silicate) – needed for pH adjustment, additive to use with hydrogen peroxide as it sequesters transition metal ions that decompose the peroxide.
  • C14H23N3O10 (DTPA) – creates stable environment for hydrogen peroxide by inactivating metal ions.

Additionally, to this chemicals, a Ca2+ source can be added to the solution. However, the Ca2+ can also originate from hard water or from paper itself. Another factor that has impact on deinking efficiency is the pH. It was shown that deinking in more alkaline environment yields in faster agglomeration of ink particles and assists in saponification reaction, thus increasing the efficiency of froth flotation. For this reason, the optimal pH value for flotation deinking is in a range between 8 and 10.

Enzymatic deinking

Enzymatic deinking is an alternative method to chemical deinking. It was experimentally proved that specific enzymes, alone or in combination with chemicals, successfully remove ink particles from wastepaper, increase the brightness of treated paper, reduce deinking expenses and is harmless way to recycle paper. However, even after many tests the method was never adapted to industrial scales. Enzymes from different classes show deinking activity, even though their target in the pulp varies. For instance, laccases and lipases directly attack ink particles and remove them from fibers, while endoglucanases and xylanases hydrolyse linkages in cellulose thus cutting the small parts of fibers containing ink and leaving the clean ones. According to different literature, cellulases show the best deinking efficiency. For this reason, we focused our work on endo-1,4-β-D-glucanase and endo-1,4-β-Xylanase M4 as these enzymes can also be secreted by Bacillus subtilis. Some chemicals have to be included in the process as well. Citrate buffer was used to provide the pH needed for enzymes to be active (pH = 4.5). Oleic acid was used as surfactant. Surfactants increase the binding capabilities of cellulases for cellulose.


Experiments

Before starting the experiments, the absorbance of our inkjet ink was determined in to determine the values that should be expected in further analysis (figure 3).

absorbance ink

Filtration based deinking

absorbance ink

To keep the scale of the experiments manageable, 50 mL falcons were chosen as containers for the small scale deinking. Firstly, the standard chemicals and water are pipetted into the falcons according to the *protocol*, afterwards pulp is added and the mixture is vortexed until it becomes slurry. Later, the falcons are incubated in a 50 °C water bath for 30 min. Although the falcons should have been shaken during the incubation time, this was not possible in our lab. After incubation, the slurry is vortexed again and the falcons are connected to the deinking apparatus as shown in figure 4. When vacuum filtration is finished, paper fibers, which stay on the filters are left to dry for one day and the flow-through is analysed further. The same procedure described above was also used for water only treatment, a treatment containing only oleic acid and oleic acid together with citrate buffer treatments.


Flow through analysis

After the flow-through is produced, it is once again vortexed and 100 μm of the samples together with water as a blank are transferred into 96 well plates in order to measure the absorbance of it with the plate reader (in our laboratory, the Tecan Infinite 200 PRO multimode reader was used). The plate reader works as spectrophotometer, it compares the light intensity of the emitted light to the light intensity of the light detected after a passage through the sample.

absorbance ink 980


After the measurements the absolute absorbance is calculated (absorbance of sample at specific wavelength – blank at specific wavelength). According to the.....the most important wavelengths to evaluate deinking efficiency are 970 and 980 nm, for this reason we concentrated on them. However, the values at these two wavelengths are almost equal, for this reason, only one of them is presented in figure 5.


Rotary evaporator

After being unable to separate ink from fibers present in flow through, it was decided to try to concentrate ink present there. For this purpose a rotary evaporator was used. The flow through solution was transferred into the apparatus in order to evaporate the water from the mixture. Afterwards, the fibers could be spun down with a centrifuge and the resulting concentrated ink solution could be taken for the absorbance scan. However, the more water was evaporated, the more ink particles strongly fused to the glass vessel’s surface and only the fibers were left. It was tried to dissolve the ink from the walls of the vessel, but we were unable to achieve this.

Grayscale

As the absorbance measurements of the flow-through were not successful, because of the residual particles and the dissolving and concentration of ink failed, scanning of the paper samples was tested. 8-bit grayscale values can vary between 0 (black paper) and 255 (white paper), all values in between describe different shades of gray thus the brightness of the paper. However, brightness alone does not describe paper quality, but it is one of the most important indicators, especially when the experiments are carried out with office waste paper. Both sides of the resulting dry paper disks were scanned in 5 different places on an office scanner. Afterwards, the images were analysed and the grayscale value obtained with the program ImageJ. (figure 6)

grayscale


Flotation-based deinking

In order to improve the deinking mechanism in our laboratory, the experiments were up-scaled. The apparatus and process itself now were much more similar to the ones used in industry (figure 7).

water vs standard

Chemical deinking was carried out using this experimental setup. Chemicals and 50 °C water were added to the beaker together with the pulp. The stirring was constant in order to mix the chemicals and fibers together. After the start of the air pump, foam, collecting ink, starts to form. For this reason, it is important to analyse foam properly. After the collection of approximately 1 L of foam, its pH was measured. The result was near 10. Later on, foam was defoamed with acetone so that the absorbance measurements could be carried out. Some fibers were still present in foam, but under proper conditions it is possible to reject them. However, after defoaming it was observed that foam contains much more fibers than it was expected and absorbance could not be measured properly.

Ink removal

Ca2+ ions are necessary in the deinking process. Previously no chemicals containing Ca2+ were added as they can originate straight from hard water or from paper itself. However, it was decided to add CaCl2 and test its effect on deinking. The experiment resulted in ink being separated completely from fibers as organic phase (figure 8).


black things


Latest deinking system

The newest deinking setup goes back to the small scale filtration-based deinking. The basic principle and used chemicals are the same as mentioned at the beginning. Only few things were changed: A kitchen mixer was used instead of vortexing machine, moreover, pulp after treatment was dried differently as it was decided to use the scanning method as the most reliable way to analyse paper deinking efficiency. For this reason bigger and flatter paper disks were needed. After filtrating the pulp-chemical mixture through the sieve, wet fibers were spread onto the lid of the well plate and were pressed lightly to flatten them. After one day, dry paper disks were scanned with the Li-Cor Odyssey infrared scanner and absorbance values at 700 nm were gained (figure 9). An office scanner was tested as well. However, it was not chosen because it may affect the value by adjusting the light when scanning.


water vs standard

The data from figure 9 proves that the deinking and its analysis system in laboratory scale was established. For this reason, tests of citrate buffer and one of the enzyme, Xylanase, were started. However, all the experiments resulted in much darker paper even when compared to simply washed paper pulp (figure 10).


water vs standard

Another problem is citrate buffer‘s crystallization. After the pulp is dried after treatment with citrate buffer, it tends to show higher values when scanning at 700 nm (meaning brighter paper). This is caused by the crystals of citrate buffer and leads to misinterpreting of results. Due to the lack of time further experiments could not be carried out. However, the laboratory scale deinking system is established and can give promising results when using enzymes to deink the paper.